Wear resistance of CAD/CAM one‐piece screw‐retained hybrid‐abutment‐crowns made from different restorative materials

The suprastructures were assembled onto the implants through titanium screws. The screw channels were sealed with Teflon tape and composite resin filling material that was polished to high-gloss. All specimens underwent 1 200 000 thermo-dynamic loading cycles with 49 N in a dual-axis chewing simulator. Elastomeric impressions were made for all specimens after 600 000 and after 1 200 000 cycles. The corresponding impressions were imaged using a laser scanning microscope and then 3D-analyzed using the software (Geomagic Wrap) to measure the volume loss of the wear area for all specimens. Statistical analysis was performed using Wilcoxon-Test regarding the two different time measurements for each material. For the analysis of the material variable, Kruskal-Wallis test was conducted followed by Mann-Whitney test.

Results

Group Z showed statistically the lowest volume loss compared to the other test materials, both after 600 000 and 1 200 000 cycles of artificial aging, with a median value of 0.002 mm3 volume loss after 1 200 000 cycles. In contrast, group E showed the highest volume loss with median values of 0.18 and 0.3 mm3 after 600 000 and 1 200 000 cycles, respectively. Artificial aging had significantly negative effect on the volume loss for all test materials. In addition, the choice of material had statistical influence on the outcome.

Conclusion

Monolithic zirconia ceramic demonstrated lower wear than that reported for enamel after simulated 5-year of clinical service, whereas all other test materials showed higher volume loss after artificial aging.

Rights

Use and reproduction:


CC BY-NC-ND 4.0

Please note that individual components of the publication may be subject to other licensing or copyright conditions.

Cite

Citation style:
Could not load citation form.